| EVA Cas 24937-78-8 |
| |
 |
| |
EVA It is a high flowability and high VA content ethylene vinylacetate copolymer (EVA) with many excellent properties, such as characteristic flexibility and elasticity, thermal stability, good low temperature resistance, good compatibility and non-toxicity, etc.
EVA16%
|
PROPERTIES
|
TEST METHOD
|
UNIT
|
Data
|
|
VA Content
|
|
%
|
16.0
|
|
Density
|
ASTM D1505
|
g/cm3
|
0.937
|
|
Melt Index MI2.16
|
ASTM D1238
|
g/10min
|
1.5
|
|
Tensile Strength (Break)
|
ASTM D638
|
Kg/cm2
|
170
|
|
Elongation at break
|
ASTM D638
|
%
|
700
|
|
Melting point
|
ASTM D-3418
|
oC
|
89
|
|
Hardness
|
ASTM D2240
|
Shore D
|
37
|
EVA 18%
|
Properties
|
Test method
|
Value
|
|
VA Content(%)
|
USI
|
18
|
|
Density(g/cm3)
|
ASTM D792
|
0.939
|
|
Melt Index (g/10min)
|
ASTM D1238
|
2.5
|
|
Tensile Strength(Molded)(Break)(kg/cm2)
|
ASTM D638
|
180
|
|
Ultimate elongation(Molded)(%)
|
ASTM D638
|
750
|
|
Low Temperature Brittleness(oC/F50)
|
ASTM D746
|
<-76
|
|
Vicat Softening Point(oC)
|
ASTM D1525
|
64
|
|
Melt Point (oC)
|
ASTM D3418
|
86
|
|
Hardness(Shore D)
|
ASTM D2240
|
36
|
EVA28%
|
PROPERTIES
|
TEST METHOD
|
UNIT
|
Data
|
|
VA Content
|
|
%
|
28.0
|
|
Density
|
ASTM D1505
|
g/cm3
|
0.954
|
|
Melt Index MI2.16
|
ASTM D1238
|
g/10min
|
15
|
|
Tensile Strength (Break)
|
ASTM D638
|
Kg/cm2
|
80
|
|
Elongation at break
|
ASTM D638
|
%
|
>800
|
|
Melting point
|
ASTM D-3418
|
oC
|
69
|
|
Hardness
|
ASTM D2240
|
Shore D
|
20
|
Mainly used in shoes, slippers, toys production
|
|
| |
|